Kyanex Shapes are highly volume stable at elevated temperatures. Besides, it has also very low impurities such as Iron Oxide, Titania and Alkalies. They have a very good resistance to thermal shocks. "Kyanex" an ideal choice for critical high temperature applications. Kyanex shapes ensures a dense uniform structure, after careful drying the shapes and sintering at high temperatures.
Kyanex is the best choice for Burner Blocks, Refractory Quarls, and Burner Throat Tiles as they must have a low Iron-Oxide to withstand spalling due to Carbon Monoxide attack. These shapes are also subjected to sharp thermal gradients, therefore they need to have excellent thermal spalling resistance. Hence shapes made out of Kyanex are ideally suited for the above application areas.
Also, our Element Holding Bricks offer low iron contamination in industry application.
BRANDS | KYANEX - 45 | KYANEX - 50 | KYANEX - 55 | KYANEX - HG | KYANEX - 60 | KYANEX - 64 | KYANEX - 70 |
Chemical Analysis | |||||||
Alumina ( Al 2 O 3 ), %, min | 45 | 50 | 55 | 58 | 60 | 64 | 70 |
Iron Oxide (Fe 2 O 3 ), %, max | 1.0 | 1.5 | 1.5 | 1 | 1.5 | 1 | 1.5 |
Physical Analysis | |||||||
Service Temperature, 0C | 1450 | 1450 | 1500 | 1550 | 1500 | 1550 | 1600 |
Bulk Density, Gm/cc, min | 2.2 | 2.25 | 2.25 | 2.25 | 2.3 | 2.5 | 2.6 |
Cold Crushing Strength Kg/cm 2 , min | 300 | 350 | 400 | 450 | 400 | 450 | 600 |
Apparent Porosity, %, max | 20 | 24 | 24 | 22 | 24 | 20 | 20 |
Thermal Properties | |||||||
Pyrometric Cone Equivalent, Orton Cone, min | 33 / 1743 | 33 / 1743 | 35 / 1785 | 38 / 1835 | 36 / 1820 | 38 / 1835 | 36 / 1820 |
Permanent Linear Change@ 14500C/3 hrs, %, max | +/-1.5 | +/-1.5 | +/-1.5 | +/-0.5 | +/-1.0 | +/-0.5 | +/-0.6 |
Thermal Spalling/No. of cycles @9500C (water quenching) | 15 | 15 | 15 | 25 | 25 | 25 | 25 |
Size Tolerence : +/-1% or 1.5mm whichever is greater.
Kynex Super is manufactured from Tabular Alumina & our in house processed raw Materials, these dense bricks have unique characteristics due to the inherent micro structural characteristics of the raw material. They have excellent resistance to wear and thermal shock and are most suitable Refractory for Sulphur Recovery Unit. They are also used to manufacturing DOME Bricks, Hexagonal Tiles, Circle Bricks & High Alumina lumps for Secondary Reformer in Fertilizer Industries.
BRANDS | KYANEX - 90T | KYANEX - 96T | KYANEX - 99 |
Chemical Analysis | |||
Alumina (Al 2 O 3 ), %, min | 90 | 96 | 99 |
Iron Oxide (Fe 2 O 3 ) %, max | 0.3 | 0.3 | 0.2 |
Physical Analysis | |||
Service temperature, 0C | 1800 | 1800 | 1850 |
Bulk Density, Gm/cc, min | 2.9 | 3 | 3.1 |
Cold Crushing Strength, Kg/cm 2 , min | 600 | 600 | 700 |
Apparent Porosity, %, max | 18 | 18 | 20 |
Thermal Properties | |||
Pyrometric Cone Equivalent, Orton Cone, min | 38 / 1835 | 38 / 1835 | 40 / 1835 |
Permanent Linear Change@ 15500C/3 hrs, %, max | +/-0.5 | +/-0.5 | +/-0.5 |
Thermal Spalling/No. of cycles @10000C | 25 | 25 | - |
Size Tolerence : +/-1% or 1.5 mm whichever is greater.
Reframul is ideal for applications in Glass Tank Furnace, Kiln Furnitures for firing ferrites, High Alumina Ceramics, Carbon Black Reactor, Cement Kiln, Burner Blocks. This has high bulk density and very low porosity making it highly volume stable.
Refractories made out of Reframul are best suited for reducing atmospheres and have resistance to slag and alkali attack. It has superior resistance to abrasion and thermal shocks. Reframul products can be used for a variety of high temperature applications where mechanical & thermal stability and resistance to creep and spalling are specified.
BRANDS | Reframul 60M | Reframul 70M |
Chemical Analysis | ||
Alumina (Al 2 O 3 ), %, min | 60 | 72 |
Iron Oxide (Fe 2 O 3 ), %, max | 0.8 | 0.3 |
Physical Analysis | ||
Service temperature, 0C | 1700 | 1750 |
Bulk Density, Gm/cc, min | 2.45 | 2.5 |
Cold Crushing Strength Kg/cm 2 , mm | 500 | 600 |
Apparent Porosity, %, max | 22 | 20 |
Thermal Properties | ||
Pyrometric Cone Equivalent, Orton Cone, min | 38 / 1835 | 38 / 1835 |
Permanent Linear Change@ 15500C/3 hrs, %, max | +/-0.5 | +/-0.3 |
Thermal Spalling/No. of cycles @10000C | 25 | 35 |
Size Tolerence : +/-1% or 1.5 mm whichever is greater.
Mullite combined with zircon offers superior refractories which are eminently suited for critical applications in Glass, Ceramic, Carbon Black, Ferrites industries. These possess high refractoriness, non wetting properties, thermal shock and abrasion resistance. These are custom made shapes with specially built in properties made with stringent quality control.
BRANDS | Refra Zirmul |
Chemical Analysis | |
Alumina (Al 2 O 3 ), % min | 75 |
Iron Oxide (Fe 2 O 3 ), % max | 0.3 |
Zirconia (ZrO 2 ), %, min | 12 |
Physical Analysis | |
Service temperature, 0C | 1760 |
Bulk Density, Gm/cc, min | 2.9 |
Cold Crushing Strength, Kg/cm 2 , min | 600 |
Apparent Porosity, %, max | 20 |
Thermal Properties | |
Pyrometric Cone Equivalent, Orton Cone, min | 38 / 1835 |
Permanent Linear Change@ 15500C/3 hrs, %, max | +/-0.5 |
Thermal Spalling/No. of cycles @10000C | 25 |
Size Tolerence : +/-1% or 1.5 mm whichever is greater.
Refra SC is a range of Oxide bonded Silicon Carbide Refractories for applications in Ceramic, Metallurgical & process Industries. Made from High purity refractory grade Silicon Carbide grains and proprietory ceramic bonds Refra SC products possess unique combination of physical and chemical properties making them ideal choice for a variety of high temperature applications.
BRANDS | Refra SiC 1 | Refra SiC 2 | Refra SiC 3 |
Chemical Analysis | |||
Silicon Carbide (SiC), %, min | 84 | 80 | 82 |
Iron Oxide (Fe 2 O 3 ), %, max | 0.8 | 1 | 1 |
Physical Properties | |||
Service temperature, 0C | 1650 | 1500 | 1450 |
Bulk Density, Gm/cc, min | 2.45 | 2.4 | 2.45 |
Cold Crushing Strength, Kg/cm 2 , min | 750 | 650 | 750 |
Apparent Porosity, %, max | 19 | 19 | 16 |
MOR at Room Temp., min | 150 | 150 | 150 |
Size Tolerence : +/-1% or 1.5 mm whichever is greater.
Refractory Shapes offer high quality fireclay and high alumina bricks ranging from 40% alumina to 85% alumina equivalent to JM series Refractory Bricks.
These bricks are manufactured as per standard specifications of clients.
BRANDS | RS - 40 | RS - 45 | RS - 50 | RS - 50 (S) | RS - 60 | RS - 60 (S) |
Chemical Analysis | ||||||
Alumina (Al 2 O 3 ), %, min. | 37 | 42 | 47 | 47 | 57 | 57 |
Iron Oxide (Fe 2 O 3 ), %, max. | 3.00 | 3.50 | 3.50 | 2.20 | 3.50 | 2.50 |
Physical Analysis | ||||||
Service temperature, 0C | 1400 | 1400 | 1400 | 1450 | 1450 | 1480 |
Bulk Density, Gm/cc, min | 2.15 | 2.2 | 2.3 | 2.25 | 2.5 | 2.35 |
Cold Crushing Strength, Kg/cm 2 , min | 300 | 350 | 450 | 450 | 500 | 450 |
Apparent Porosity, %, max | 22 | 22 | 22 | 21 | 22 | 22 |
Thermal Properties | ||||||
Pyrometric Cone Equivalent, Orton Cone, min | 29/1659 | 30/1665 | 31/1683 | 32/1717 | 35/1785 | 35/1785 |
Refractoriness Under Load, Ta, 0C | 1340 | 1350 | 1380 | 1400 | 1400 | 1450 |
Permanent Linear Change@ 14000C/3 hrs, %, max | +/-0.8 | +/-1.0 | +/-1.0 | +/-1.0 | +/-1.0 | +/-0.75 |
BRANDS | RS 70 | RS 70(S) | RS 70P | RS 80 | RS 85 | RS 85P |
Chemical Analysis | ||||||
Alumina (Al 2 O 3 ), %, min | 66 | 67 | 67 | 77 | 82 | 82 |
Iron Oxide (Fe 2 O 3 ), %, max | 3.5 | 3 | 2.8 | 1.8 | 1.8 | 1.8 |
P 2 O 5 %, max | 1.8 | 1.8 | ||||
Physical Analysis | ||||||
Service temperature, 0C | 1450 | 1450 | 1480 | 1550 | 1600 | 1600 |
Bulk Density, Gm/cc, min | 2.6 | 2.55 | 2.6 | 2.75 | 2.78 | 2.8 |
Cold Crushing Strength, Kg/cm 2 , min | 600 | 600 | 700 | 750 | 800 | 800 |
Apparent Porosity, %, max | 22 | 22 | 20 | 22 | 19 | 18 |
Thermal Properties | ||||||
Pyrometric Cone Equivalent, Orton Cone, min | 36/1804 | 36/1804 | 36/1804 | 37/1820 | 37/1820 | 37/1820 |
Refractoriness Under Load, Ta, 0C | 1430 | 1430 | 1450 | 1500 | 1500 | 1500 |
Permanent Linear Change@ 14500C/3 hrs, %, max | +/-2.0 | +/-1.75 | +/-1.75 | +/-0.80 | +/-0.8 | +/-0.8 |
Size Tolerence : +/-1% or 1.5 mm whichever is greater.
Note : Phosphate Bonded bricks are commonly used in chemically corrosive environments.
BRANDS | Xlite CF | Xlite HF |
Chemical Analysis | ||
Alumina (Al 2 O 3 ), %, min | 28 | 30 |
Iron Oxide (Fe 2 O 3 ), %, max | 2 | 2 |
Physical Analysis | ||
Service temperature, 0C | 1100 | 1200 |
Bulk Density, Gm/cc, max | 0.75 - 0.8 | 0.85 - 0.9 |
Cold Crushing Strength, Kg/cm 2 , min | 15 | 18 |
Apparent Porosity, %, min | 70 | 65 |
Thermal Properties | Permanent Linear Change@ 10000C/3 hrs, %, max | +/-1.5 | - |
Permanent Linear Change@ 11000C/3 hrs, %, max | - | +/-1.5 |
Thermal Conductivity @ 6000C HF | 0.19 | 0.25 |
Size Tolerance: + 1% or + 1.5mm whichever is greater.
Xlite series of insulating bricks are specially formulated with independent pores so as to ensure maximum insulating efficiency. These bricks are suitable for hot face insulation since gas permeation is prevented. Apart from low thermal conductivity, bricks have low density, high strength, high PCE and low iron content.
Xlite is a unique development made with energy saving as the prime consideration. Xlite is a foamed Sillimanite shaped refractory - a hybrid of Sillimanite refractory insulation brick incorporating the best insulating properties. Sillimanite being highly volume stable at elevated temperatures, extremely intricate shapes can be made out of Xlite with close dimensional tolerances. Xlite being foamed, has strengths greater than any conventional insulation brick of corresponding densities. Foamed structure enables Xlite for a better thermal shock resistance. Xlite range can be safely used for service temperatures upto 1650°C for hot face linings.
BRANDS | Xlite 8 | Xlite 10 | Xlite 12 | Xlite 14 |
Chemical Analysis | ||||
Alumina (Al 2 O 3 ), %, min | 58 | 58 | 58 | 58 |
Iron Oxide (Fe 2 O 3 ), %, max | 1 | 1 | 1 | 1 |
Physical Analysis | ||||
Service temperature, 0C | 1500 | 1650 | 1650 | 1650 |
Bulk Density, Gm/cc, max | 0.90 | 1.10 | 1.30 | 1.50 |
Cold Crushing Strength, Kg/cm 2 , min | 25 | 40 | 60 | 90 |
Apparent Porosity, %, min | 65 | 60 | 60 | 55 |
Thermal Properties | ||||
Pyrometric Cone Equivalent, Orton Cone, min | 37 | 37 | 37 | 37 |
Permanent Linear Change, %, max | +/-1.0 @ 14500C/3 hrs | +/-1.0 @ 14500C/3 hrs | +/-1.0 @ 14500C/3 hrs | +/-1.0 @ 14500C/3 hrs | Thermal Conductivity @ 8000C HF | 0.45 | 0.40 | 0.45 | 0.55 |
Size Tolerence : +/-1% or 1.5 mm whichever is greater.
BRANDS | Xlite 23 | Xlite 26 | Xlite 28 | Xlite 30 |
Chemical Analysis | ||||
Alumina (Al 2 O 3 ), %, min | 37 | 58 | 65 | 71 |
Iron Oxide (Fe 2 O 3 ), %, max. | 1.2 | 1 | 0.6 | 0.5 |
Physical Analysis | ||||
Service temperature, 0C | 1260 | 1430 | 1540 | 1650 |
Bulk Density, Gm/cc, max | 0.60 | 0.85 | 0.95 | 1.10 |
Cold Crushing Strength, Kg/cm 2 , min | 10 | 20 | 25 | 35 |
Apparent Porosity, %, min | 65 | 55 | 50 | 45 |
Thermal Properties | ||||
Permanent Linear Change, %, max | +/-0.5 @ 12300C/5 hrs | +/-0.3 @ 14000C/5 hrs | +/-0.5 @ 15000C/5 hrs | +/-0.8 @ 16000C/5 hrs | Thermal Conductivity @ 8000C HF (Kcal/m/hr/degC) | 0.15 | 0.27 | 0.3 | 0.33 |
Size Tolerence : +/-1% or 1.5 mm whichever is greater.
Many speciality application in Fertilizers, Refineries, Energy Industries, Carbon & Chemical Industries are in complicated shapes of High performance refractories like Ceramic Ferrules, Lances, Shrouds, Small dia tube which requires meticulous care in selection of raw material manufacture to achieve stringent properties especially dimensional tolerance, thermal shock resistance and high durability in services, Refractory Shapes makes these special shapes in 60 to 94% Alumina categories, Zircon meeting the stringent specification of the user industries.
BRANDS | Kyanex SC | Kyanex 90 SC | Kyanex 96 SC | Kyanex Z SC |
Chemical Analysis | ||||
Alumina (Al 2 O 3 ), %, min | 58 | 90 | 94 | - |
Iron Oxide (Fe 2 O 3 ), %, max | 1 | 0.3 | 0.3 | 0.5 |
Silica (SiO 2 ) | 40 | 6 | - | 38 |
Zirconia (ZrO 2 ), %, min | - | - | - | 58 |
Physical Analysis | ||||
Service temperature, 0C | 1500 | 1600 | 1650 | 1800 |
Bulk Density, Gm/cc, min | 2.2 | 2.65 | 2.65 | 2.8 |
Cold Crushing Strength, Kg/cm 2 , min | 450 | 500 | 550 | 700 |
Apparent Porosity, %, max | 20 | 18 | 18 | 20 |
Thermal Properties | ||||
Permanent Linear Change@ 15000C/3 hrs, %, max | +/-1.0 | +/-0.5 | +/-0.5 | +/-0.5 |
Size Tolerence : +/-1% or 1.5 mm whichever is greater.
Mortars (Insulating)
These mortars are used as jointing material for High Alumina Bricks and Insulation Bricks.
Some of the mortars are supplied as two-component system, where liquid binder is separately provided with powder material. In such a case, liquid component should be used only as per our recommendation. Where water is used as a liquid component, the amount of water used should be such that it results in trowelling consistency.
BRANDS | RSM-Insul | RS HS Mortar | Xlite Mortar |
Chemical Analysis | |||
Al2O3% min. | 20 | 40 | 50 |
Fe2O3% max. | 2.0 | 1.5 | 1.0 |
SiO2% | 66.8 | 50 | 43 |
CaO% | 0.3 | - | - |
Physical Properties | |||
Service Temp. ˚C | 1350 | 1550 | 1600 |
Sintering Temp. ˚C | 1100 | 1100 | 1100 |
Grain Size | 1.0 | 0.5 | 0.5 |
% Binder for trowelling consistency | 70 - 75 | 25 - 30 | 33 - 35 |
CCS, Kg/cm2 | - | 14 | 16 |
Thermal Properties | |||
PCE Orton/ ˚C | 18/1522 | 31/1683 | 32/1717 |
Packaging: 40 Kgs Bag
Storage Life: 12 months
BRANDS | RSM - 60 | RSM – 60S | RSM - 70 | RSM – 80 | RSM – 90 | RSM – 99 |
Chemical Analysis | ||||||
Al2O3 % min. | 60 | 60 | 70 | 80 | 90 | 96 |
Fe2O3 % max. | 3.5 | 2.2 | 3.5 | 3.5 | 0.3 | 0.3 |
SiO2 % | 25.4 | 29 | 17 | 10.1 | 6.3 | 0.8 |
CaO % | 0.3 | 0.5 | 0.5 | 0.7 | 0.1 | 0.1 |
Physical Properties | ||||||
Service Temp. ˚C | 1600 | 1650 | 1700 | 1700 | 1750 | 1800 |
Sintering Temp. ˚C | 1100 | 1100 | 1100 | 1100 | 1100 | 1100 |
Grain Size | 0.5 | 0.5 | 0.5 | 0.5 | 0.5 | 0.5 |
Water for trowelling consistency, % | 21 - 24 | 25 - 30 | 21 - 24 | 18 - 22 | 35 - 40 | 50 - 60 |
Thermal Properties | ||||||
PCE Orton / ˚C | 33 / 1743 | 34 / 1763 | 35 / 1785 | 34 / 1763 | 38 / 1835 | 38 / 1835 |
Packaging: 50 Kgs Bag
Storage Life: 12 months
Common Note : The above physical & thermal properties can be boosted as per client requirement by using superior in house processed raw materials.